首页 > 最新消息 > 2008 > 优必龙高流动透明阻燃PC级EFT3200H

News

优必龙高流动透明阻燃PC级EFT3200H
"iupilon EFT3200H" flame retardant PC with excellent flowability and transparency

2008年1月15日

优必龙EFT3200H是我公司采用液流控制技术开发的高流动透明阻燃PC树脂。不仅保留了PC树脂优越的透明性,还取得了2.0mmV-0,成功进行了改良,比普通喷射级别(非阻燃)具备更好的流动性。

各种透明色可供您选择,对必须具备阻燃性的产品的设计自由度将大大提高。

另外,还有注重冲击特性的EFT3200、碾压成型用的EFT2300(相当于3mmV-0)等型号可供选择。

"iupilon EFT3200H" is a new flame retardant PC developed with our rheology control technology. EFT3200H is classified V-0(2mm) with good transparency and excellent flowability.
Various transparent colors help the design of your products.
EFT3200, the high impact type, and EFT2300 for extrusion molding are also available.

特点/Feature

1. 不使用溴素系阻燃剂、磷系阻燃剂,环保型阻燃级别。
  Nonbrominated and nonphosphorous flame retardant

2.具备优越的透明性。
  Good transparency

3.具备高流动性。
  Excellent flowability

普通物性/Typical properties

项目 试验方法 试验条件 单位 透明环保阻燃
高流动性
卤素阻燃 普通非阻燃
iupilon
EFT3200H
iupilon
N-5
iupilon
S3000R
物理性质
密度 ISO 1183 - g/cm3 1.20 1.28 1.20
液流特性
2mm钢条流动长度 MEP法
MEP法喷射压力200MPa
280℃ mm 270 250 250
300℃ mm 390 380 370
320℃ mm 540 500 490
机械特性
屈服拉伸应力 ISO527-1
527-2
- MPa 62 68 62
屈服拉伸形变 % 6.5 6.6 6.7
拉伸断裂形变 % 100 120.0 120.0
拉伸弹性模数 MPa 2,300 2,800 2,300
弯曲强度 ISO 178 - MPa 93 99 93
弯曲弹性模数 2,300 2,300 2,300
带槽口却贝冲击强度 ISO 179-1
179-2
- kJ/m2 14 6 67
不带槽口却贝冲击强度 NB NB NB
带槽口IZOD冲击强度 ASTM D256 - J/m 560 60 800
热特性
载荷挠曲温度 ISO75-1,75-2 1.80MPa 122 125 124
0.45MPa 135 141 139
UL94阻燃性 UL94 2mmt - V-0 V-0 HB
光学特性
全光线透过率 ASTM D1003 2mmt % 88 90 89
3mmt % 88 90 89
Haze ASTM D1003 2mmt % 0.4 0.3 0.4
3mmt % 0.4 0.3 0.4
标准成型条件
材料干燥 干燥温度 120
干燥时间 时间 4~8
成型温度 模具温度 70~100 70~100 80~100
汽缸温度 280~310 270~300 270~300

该物性表中记载的数据为测量值,并非规格值。

Properties Test Method Terms Units Non brominated
Non phosphorous
High flow
Reference
(Brominated FR)
General Purpose
(No flameretardant)
iupilon
EFT3200H
iupilon
N-5
iupilon
S3000R
Physical properties
Density ISO 1183 - g/cm3 1.20 1.28 1.20
Rheological properties
2mmt Bar flow length MEP method
Injection Pressure
200MPa
280°C mm 270 250 250
300°C mm 390 380 370
320°C mm 540 500 490
Mechanical properties
Yield stress ISO527-1
527-2
- MPa 62 68 62
Yield strain % 6.5 6.6 6.7
Nominal strain at break % 100 120.0 120.0
Tensile modulus MPa 2,300 2,800 2,300
Flexural strength ISO 178 - MPa 93 99 93
Flexural modulus 2,300 2,300 2,300
Charpy notched impact strength ISO 179-1
179-2
- kJ/m2 14 6 67
Charpy impact strength NB NB NB
IZOD notched impact strength ASTM D256 - J/m 560 60 800
Thermal properties
Temperature of deflection
under load
ISO75-1,75-2 1.80MPa °C 122 125 124
0.45MPa °C 135 141 139
Flammability UL94 2mmt - V-0 V-0 HB
Optical properties (Natural color)
Total transmittance ASTM D1003 2mmt % 88 90 89
3mmt % 88 90 89
Haze ASTM D1003 2mmt % 0.4 0.3 0.4
3mmt % 0.4 0.3 0.4
Molding conditions
Drying Temperature °C 120
Time Hrs 4~8
Tool temperature   °C 70~100 70~100 80~100
Melt temperature   °C 280~310 270~300 270~300

The listed properties are portrayed as general information only and are not product specifications.
Mitsubishi Engineering-Plastics disclaims any liability in connection with the use of the information in this table.

产品信息

  • ポリカーボネート樹脂(PC樹脂)ユーピロンノバレックスザンター
  • ポリブチレン テレフタレート樹脂 (PBT樹脂) ノバデュラン
  • ポリアセタール樹脂(POM樹脂)ユピタール
  • 変性ポリフェニレン エーテル樹脂(m-PPE樹脂)ユピエースレマロイ
  • 高性能ポリアミド樹脂(PA樹脂)レニー